金属声屏障由于被长年应用于室外环境当中，必定会长年遭受到风吹雨打的浸蚀，而再加之阳光、气温等条件的影响，就会使得产品本身产生出化学反应——生成氧化铁物质（俗称锈）,这就要求我们再生产加工金属声屏障的过程中，做好防腐措施，可通过选用包塑、镀锌、喷塑等方式进行处理，以提高产品的防腐性以及使用寿命。然而有些不良商家利益熏心，为了追求更大利润，就会偷工减料或是防腐手段处理不到位，导致声屏障产品出现生锈、折断的现象发生，出现这种问题，我们该如何解决呢？

Because the metal sound barrier is used in the outdoor environment for a long time, it will inevitably suffer the erosion of wind and rain for a long time, and the influence of the conditions of sunshine and temperature will cause the product itself to produce chemical reaction - forming iron oxide (commonly known as rust). It is necessary for us to make a good anticorrosion measure in the process of producing and processing metal sound barrier. Zinc plating, spray molding and so on are processed to improve the corrosion resistance and service life of products. However, some bad business interests, in order to pursue greater profits, will steal material or corrosion treatment is not in place, resulting in the emergence of sound barrier products rusty, broken phenomenon, this problem, how should we solve it?

如若声屏障本身出现破损情况，那么，我们就要对声屏障的本身进行即时修复，以保障声屏障产品的功能性，方便接下来的使用。修复的材料选用与声屏障本身材质相匹配的材料进行补缺，倘若应用的是低碳钢结构的声屏障设施的话，就要选用低碳钢材质进行补缺，利用电氧焊、氩弧焊等方式将其固定于缺口中，当进行完这一流程之后，声屏障本身的性能便会恢复如初；如若是声屏障防腐上出现问题，我们就应当选用包塑、镀锌等方式进行声屏障外围的保护，从而根本上杜绝生锈情况的再度发生。

If the sound barrier itself is damaged, then we need to repair the sound barrier itself immediately to ensure the function of the sound barrier products and facilitate the use of the next. The material for repair is used to complement the material that matches the material of the sound barrier itself. If the sound barrier facilities of low carbon steel are used, the material of low carbon steel should be used to fill the gap, and it will be fixed in the gap by means of electric oxygen welding and argon arc welding. When this process is finished, the performance of the sound barrier itself will be restored as early as the sound barrier anticorrosion. If there is any problem, we should use plastic wrap and galvanizing to protect the outside of the sound barrier, so as to eliminate the recurrence of rust.